Hello analogkid2digitalman:
Thank you also for this information. The person I did the work for has retired. I will see if this work has been picked up by someone else. take care,
Steved
Boo1:
Thanks for the reply, I appreciate the information. I went to schaeffer's web site and will contact them. As for your questions:
- The temperature range is from RT to 395C.
- It is intermittant, every 80 minutes, it heats and then cools - assuming the line doesn't stop.
- There are...
Hello: We have a coating operation the requires the curing of the product at 395 C. The present lubricant is applied as a grease and eventually (3 months) turns to a powder that can contaminate our product. This requires an extensive and expensive oven cleaning approximately every 3 months. Does...
Hello:
The only familiarity I have with nickel on stainless steel was for an elecroforming application (about 8 years ago). Stainless steel is very passive and our deposit used to fall off in the tank. The solution was a Woods nickel strike (very low pH). Another suggestion is a Sulfamate...
Hello: Due to print specifications, we are required to grit blast our substrates prior to powder coating. The powder is a mixture of teflon and SiC. After curing, some rolls have a defect that we call grit or protrusions. Analysis of defects shows grit or SiC. Has anyone seen this type of...