Hi,
I have a drawing that calls out ASTM E1417 Type I method A, form d, class 2. Is solvent remover class only specified on ASTM E1417 Type I, Method C or could it be specified if "form d" (nonaqueous) developer is used?
In AMS 2774, does anyone know what the metallurgical reason for the higher annealing temperature at 2050 F temperature for alloy 625 if brazing will follow? Normally, annealing would be at 1900 F, but footnote 9 in rev G requires a 2050 F anneal if high-temperature brazing is to follow.
Where do I measure underfill from when I have mismatch? In this attached figure, should it be "A" or "B"? I can't find guidance in AWS D17.1.https://files.engineering.com/getfile.aspx?folder=37b4d1fb-93dc-447a-9062-0c9789ce55f6&file=welder_cert_7773.jpg
I am having trouble finding a supplier with the capability of making large diameter (~55 ") flash welded rings in high temperature alloys such as RA 330 and Inconel 601. Does anyone have any suggestions?
Would you interpret this symbol this way or is this incorrect? Should I have two symbols instead?https://files.engineering.com/getfile.aspx?folder=bde4cf37-a233-4c4c-abee-79fda1bd023e&file=New_Microsoft_PowerPoint_Presentation.pptx
We are using this alloy called VACOFLUX 9CR. Unfortunately, the manufacturer does not have fatigue characterization of it. Does anyone know of a similar alloy that may have fatigue data associated with it?
I have a situation where there are two dissimilar metals in contact with each other. They will be exposed to cryogenic temperatures, so there is a possibility of moisture wetting. I know the approximate potential in sea water service. I was looking for a way to conservatively estimate the...
I am trying to help my old high school out. Their tensile test machine broke down. I am trying to get a new one for them. Any advice on where I can purchase low cost, but reliable tensile testing machines that can test metals?
When a groove weld joint is already partially beveled and a you specify a symbol with a v groove but do not specify the depth of the groove, is it interpreted as weld through the bevel into the backside or just start from the bottom of the v-groove. See my alternate interpretations in the...
Is there anything in NAVSEA tech pub 248 that states that my welder performance qualification test assembly can deviate from the joint configurations shown in Table XI?
Does anyone know companies (preferably in southern California) who can perform helium gas purity testing to CGA-G-9.1. We need to double check our gas vendor.
Is there any reason why we couldn't touch up scratches on a MIL DTL 5541 Class 3 with Class 1A? Either class 3 or 1A properties will suffice. I just want to know if there will be some incompatibility issues that could deteriorate the existing class 3 coating.